In this work we have prepared lead-free ceramics BaTiO3, CaTiO3 and Ba0.85Ca0.15Ti0.9Zr0.1O3 successfully from different raw materials barium carbonate (BaCO3) calcium carbonate (CaCO3) dioxide of titanium (TiO2) and zirconium dioxide (ZrO2) by the conventional solid state reaction technique at different sintering temperatures. These materials are mixed for 6 hours and sintered at temperatures of 1200 °C to 1300 °C for 2 hours. The sintering temperature has been varied to study its effects on microstructure and structural properties. Structural parameters were analyzed using X-ray diffraction (XRD), scanning electron microscope (SEM). Differential thermal analysis coupled with thermogravimetric analysis (ATG-ATD) was performed mainly to follow the process of precursor decomposition and formation of the perovskite phase. The XRD analysis results clearly show the synthesis of the perovskite phase as well as highlighting the formation of the Ba2TiO4 phase in addition to the BaTiO3 phase. The diffractogram obtained shows that the BCTZ symmetry is both Cubic with a space group Pm-3m and orthorhombic with a space group R3m. The calculated phase rates are: 10% and 90% respectively.

L’objectif abordé dans notre travail est la réalisation par mélange à l’état fondu et caractérisation des systèmes hybrides à base d’une matrice thermoplastique, le polypropylène et d’une argile lamellaire, la kaolinite avec et sans agent compatibilisant "PP-g-MA", et ce dans le but d’améliorer la compatibilité entre les deux composants incompatible.La caractérisation des composites PP/kaolin est faite au travers de moyens d’investigations classiques tels que la détermination des propriétés mécaniques (traction, choc) et thermiques (DSC). Par ailleurs, les propriétés mécaniques des composites obtenus, ont été très influencées par l’état de dispersion de la charge au sein de la matrice et par les faibles interactions PP / kaolinit